Question

For a fiber composite with a fiber-matrix bond shear strength of 37.4 MPa and a critical...

For a fiber composite with a fiber-matrix bond shear strength of 37.4 MPa and a critical fiber length-fiber diameter ratio of 50, what is the tensile strength of the fibers?

Homework Answers

Answer #1

An expression for critical fiber length is given as-

where,

- Critical fiber length

- ultimate tensile strength

- Fiber diameter

- fiber-matrix bond strength.(37.4 MPa)

So,

put all values,

Thank you,

Know the answer?
Your Answer:

Post as a guest

Your Name:

What's your source?

Earn Coins

Coins can be redeemed for fabulous gifts.

Not the answer you're looking for?
Ask your own homework help question
Similar Questions
A unidirectional composite is made up of: 25 volume % of fiber type 1 (E =...
A unidirectional composite is made up of: 25 volume % of fiber type 1 (E = 300 GPa, Poisson's ratio n = 0.25), 25 volume % of fiber type 2 (E = 100GPa, Poisson's ratio n = 0.25), and 50 volume % of a matrix (E = 60 GPa and n = 0.30). The tensile strength of fiber type 1 is 500MPa, that of fiber type 2 is 100MPa, and that of the matrix is 200MPa. Draw a tensile stress-...
16.0 (40 pts) The metal matrix of the composite described in Prob. 15 is known to...
16.0 (40 pts) The metal matrix of the composite described in Prob. 15 is known to contain internal flaws up to 2.9 E-6 m is size while the fiber has edge notches up to 8.4 E-6 m. Determine (a) which cracks first, the matrix or the fiber and (b) determine the critical composite stress (iso-strain and applied in the direction of the fibers) at which the first critical crack forms. Assume Y=1 and Kic (matrix) and Kic(fiber) are 7.8 and...
Polymer composite materials have gained popularity because they have high strength to weight ratios and are...
Polymer composite materials have gained popularity because they have high strength to weight ratios and are relatively easy and inexpensive to manufacture. However, their nondegradable nature has prompted development of environmentally friendly composites using natural materials. An article reported that for a sample of 10 specimens with 2% fiber content, the sample mean tensile strength (MPa) was 51.9 and the sample standard deviation was 1.2. Suppose the true average strength for 0% fibers (pure cellulose) is known to be 48...
Polymer composite materials have gained popularity because they have high strength to weight ratios and are...
Polymer composite materials have gained popularity because they have high strength to weight ratios and are relatively easy and inexpensive to manufacture. However, their nondegradable nature has prompted development of environmentally friendly composites using natural materials. An article reported that for a sample of 10 specimens with 2% fiber content, the sample mean tensile strength (MPa) was 51.7 and the sample standard deviation was 1.4. Suppose the true average strength for 0% fibers (pure cellulose) is known to be 48...
Polymer composite materials have gained popularity because they have high strength to weight ratios and are...
Polymer composite materials have gained popularity because they have high strength to weight ratios and are relatively easy and inexpensive to manufacture. However, their nondegradable nature has prompted development of environmentally friendly composites using natural materials. An article reported that for a sample of 10 specimens with 2% fiber content, the sample mean tensile strength (MPa) was 51.5 and the sample standard deviation was 1.3. Suppose the true average strength for 0% fibers (pure cellulose) is known to be 48...
How does shear strength differ between a sand sample at a depth of 10 feet versus...
How does shear strength differ between a sand sample at a depth of 10 feet versus the same soil at a depth of 50 feet? What is the impact on peak and critical state shear? Critical state void ratio?
An E-glass fiber (Ef = 1.0x107 psi, Tensile strength Sften = 5x105 psi, r=2.6 gm/cm3) unidirectional...
An E-glass fiber (Ef = 1.0x107 psi, Tensile strength Sften = 5x105 psi, r=2.6 gm/cm3) unidirectional fabric (600 gm/m2) has a volume fiber fraction of 0.4. The matrix is vinyl ester resin (Em = 4x105 psi, Tensile strength Smten = 1.2x104 psi, r = 1.15 gm/cm3). What is the density of the laminate? What is the Mass fiber fraction Mf? What is the longitudinal modulus of elasticity of the laminate? What is the tensile strength of the laminate? What is...
What instrument do you use to test fiber-matrix interface strength?
What instrument do you use to test fiber-matrix interface strength?
Hot-pressed Si3N4has a tensile strength of 550 MPa. Flaws are present due to porosity remaining in...
Hot-pressed Si3N4has a tensile strength of 550 MPa. Flaws are present due to porosity remaining in the part; the radius of curvature of these flaws is determined to be 0.005 cm. The part should be capable of withstanding an applied stress of 200 MPa. What is the maximum length of flaws that can be tolerated?
Consider the following observations on shear strength (MPa) of a joint bonded in a particular manner....
Consider the following observations on shear strength (MPa) of a joint bonded in a particular manner. 21.2      40.4      16.4      73.6      36.6      110.0      30.0      4.4      33.1      66.7      81.5   a) What are the values of the fourths? (Enter your answers to two decimal places.) lower fourth     MPa upper fourth     MPa What is the value of fs? = MPa Comment on its features. (Select all that apply.) The variation seems quite large. The data is symmetric. There are outliers. There is a slight...