Question

(a) Determine the critical crack length for a center crack in a plate of aluminum alloy...

(a) Determine the critical crack length for a center crack in a plate of aluminum alloy under uniaxial tension. The critical stress intensity factor of this alloy is 25.5 M P a ⋅ m. The plate width and thickness are 250 mm and 10 mm, respectively. Along the length direction, a 1000 kN force is applied. Assume Y = π. The Young’s modulus is 85 GPa. The yield strength is 105 MPa. (b) What is the critical crack-tip opening displacement (CTOD)? (c) What is the critical crack-tip plastic/process zone size?

Engineering   Civil-Engineering   
0 0
Add a commentTranscribed image text
Next >

Homework Answers

Answer #1


0 0
Know the answer?
Your Answer:

Post as a guest

Your Name:

What's your source?

Earn Coins

Coins can be redeemed for fabulous gifts.

Log In

Sign Up

Not the answer you're looking for?
Ask your own homework help question
Similar Questions
A center-cracked plate is loaded in tension and has dimensions of b = 40 mm, t...
A center-cracked plate is loaded in tension and has dimensions of b = 40 mm, t = 5 mm, and large h, and it contains an initial crack of length 2ai = 8 mm. A zero-to-maximum cyclic load of 80 kN is applied, and the material has σY= 320 MPa, KIC= 40 MPa√m. (a)What is the crack length for plastic yielding, aY? (b)What is the crack length for brittle fracture, ac? (c) Will the plate fail by i. plastic yielding...
By means of finite elements (flat stress condition) it was determined that the plastic zone of...
By means of finite elements (flat stress condition) it was determined that the plastic zone of a crack located in a semi-infinite aluminum sheet is 0.270 mm and this is contained in a central through-fissure of 10 mm in length. The material properties are: σy = 600 MPa and E = 80 GPa. Calculate the critical CTOD and the critical effort.
For a rectangular bar of a new type of metal alloy with initial dimensions of 8...
For a rectangular bar of a new type of metal alloy with initial dimensions of 8 mm wide and 45 mm long, what will be the ratio of the change in width to the change in length upon application of a tensile stress of 275 MPa if the Young’s modulus has been found to be 267 GPa and Poisson’s ratio is 0.28? Circle your answer
For a bronze alloy, the stress at which plastic deformation begins is 284 MPa and the...
For a bronze alloy, the stress at which plastic deformation begins is 284 MPa and the modulus of elasticity is 123 GPa. (a) What is the maximum load that can be applied to a specimen having a cross-sectional area of 305 mm2 without plastic deformation? (b) If the original specimen length is 112 mm, what is the maximum length to which it may be stretched without causing plastic deformation? (a) N (b) mm
For a bronze alloy, the stress at which plastic deformation begins is 270 MPa and the...
For a bronze alloy, the stress at which plastic deformation begins is 270 MPa and the modulus of elasticity is 125 GPa. (a) What is the maximum load that can be applied to a specimen having a cross-sectional area of 303 mm2 without plastic deformation? (b) If the original specimen length is 102 mm, what is the maximum length to which it may be stretched without causing plastic deformation
A crack, 1 mm long on the surface, is discovered in a 6061-T651 Al alloy cylindrical...
A crack, 1 mm long on the surface, is discovered in a 6061-T651 Al alloy cylindrical support beam using the eddy current technique. The beam’s diameter is 10 cm. The beam is situated in a aircraft such that it is under a uniform normal stress that is fluctuating. The maximum stress on the beam is 300 MPa. What shape would you assume the crack has? What length would would the crack need to grow to along the surface by fatigue...
A center-cracked panel with an initial crack length of 0.010 mm is subjected to a tensile...
A center-cracked panel with an initial crack length of 0.010 mm is subjected to a tensile cyclic stress between 25 and 125 MPa for 350000 cycles. The panel is then subjected to a tensile cycle stress between 0 and 250 MPa. How many of the larger stress amplitude cycles can be sustained before failure? The material has a fracture toughness of 25 MPa?m and material constants n = 3.1 and C = 1.8 x 10-10 for these units.
I need it ASAp. if u are sure please do with clean hand writing.thanks A large...
I need it ASAp. if u are sure please do with clean hand writing.thanks A large flat plate is subjected to constant amplitude uniaxial cyclic tensile and compressive stresses. Compute the critical crack length if the fatigue life must be at least 3x106 cycles. Assume the initial maximum edge surface crack length to be 1.1 mm, and a maximum tensile stress of 160 MPa. Assume m=3.0, A=1.4x10-13MPa in meter units, and Y=1.2.
A lightweight design of turbofan disc for an aero-engine has failed during a run-up test. The...
A lightweight design of turbofan disc for an aero-engine has failed during a run-up test. The disc can be taken to be of uniform thickness 125mm and has a central hole of diameter 300mm and an outer rim diameter of 700mm. The outer rim was loaded with 40 blades, each of mass 5kg evenly pitched around the periphery at an effective radius of 400mm. The disc had previously survived a run-up test with no blades attached. The titanium alloy used...
The 7-mm-thick base plate of an iron is made of an aluminum alloy (? = 2,700...
The 7-mm-thick base plate of an iron is made of an aluminum alloy (? = 2,700 kgm-3; c = 950 Jkg-1K-1; k = 200 Wm-1K-1; ? = 0.8), and has outer surface area of 0.04 m2, perimeter of 0.7 m, and maximum length of 0.3 m. An electrical resistance heater applies a uniform heat flux of 12.5 kWm-2 to the inner surface of the base plate when the iron is turned on. The outer surface of the base plate is...